Hot rolled Steel Plates, Sheets and Coils (Armour steel)

Hot rolled Steel Plates, Hot rolled Steel Plates Sheet Suppliers, Hot rolled Steel Plates Coils Manufacturer, Hot rolled Steel Plates Exporter in India.

EN 1522 PM 2000/EN 1522 Plates, Hot rolled Steel Plates Suppliers, PM 2000/EN 1522 Steel Plates, Hot rolled Steel Sheets, Hot rolled Steel Coils, Armour steel Exporter.

Hot Rolled Steel Plates, Sheets & Coils are manufactured in accordance with the prevailing quality standards of the industry using precision production techniques. These are manufactured and designed using qualitative raw material, which meets the quality standards. These products can be customized as per the clients’ requirements available at affordable price.
These Hot Rolled Steel Plates, Sheets, Coils are made to resist heavy weights and pressure conditions which are available in different specifications. Our range finds usage in structural, mechanical and engineering applications.

Applications : Doors, window frames, walls, Bank counters and vaults, Money exchange offices, Cars, security vans, Secured containers, Shooting gallery devices, Military vehicles and equipment.

Specifications :

Chemical Composition	Mechanical Properties	HARDNESS-200 BHN (Min)
GRADE	C % Max	Min % Max	P % Max	S% Max	SI % Ma
SAIL HARD	0.23	1.6	0.050	0.050	0.50
AI0.10 max, Cr 0.65 max, Nb +V+Ti0.15 Max

Heavy plates and sheets. Thickness Tolerances.

Heavy plates Thickness mm	Upper tolerance mm	Sheets Thickness mm	Upper tolerance, width-wise mm
			-1200	1201 – 1500
6.00 – 6.99	0.74	2.50 – 3.00	0.30	0.32
7.00 – 7.99	0.76	3.01 – 4.00	0.32	0.36
8.00 – 9.99	0.80	4.01 – 5.00	0.36	0.40
10.00 – 11.99	0.90	5.01 – 6.00	0.40	0.42
12.00 – 14.99	1.00	6.01 – 6.50	0.44	0.44
15.00 – 19.99	1.10
20.00 – 24.99	1.20
25.00 – 29.99	1.30
30.00	1.40
Lower thickness tolerance for both plates and sheets is 0 mm.

Chemical composition :

	C	Si	Mn	P	S	Cr	NI	Mo	B
Ramor 400	0.24	0.70	1.50	0.020	0.015	1.00	1.00	0.70	0.005
Ramor 500	0.32	0.70	1.50	0.020	0.015	1.00	2.00	0.70	0.005

The steel is aluminium-killed and grain-refined.

Mechanical properties :

	R MPa	R MPa	A %	HB	t °C	Cha
Ramor 400	1100	1300	8	360 – 450	-40	20
Ramor 500	1450	1700	7	480 – 560	-40	20
with 10 x 10 standard test pieces. When testing thicknesses less than 10 mm, the width of the test pieces corresponds with the plate thickness and the impact strength values decrease in direct relation to the surface area of the test piece.

Testing

Test	According to standard	Test frequency
Tensile test	EN 10002-1	Typical values or according to agreement.
Brinell hardness test	EN ISO 6506-1	Each heat treatment individually.
Charpy impact test	EN 10045-1	Typical values or according to agreement.
Ballistic protection	PM2000/EN 1522 Stanag 4569	Typical values according to approval tests.

Recommended minimum plate thickness for different protection classes, Ramor 500


Standard / Norm	Protection level	Threat	Weight of the bullet Grams	Distance Meters	Obliquity Degrees	Striking velocity m/s	Recommended minimun thickness mm
EN 1522 PM 2000/EN 1522	FB3 PM4	.357 Magnum .357 Magnum .44 Magnum	10.20 10.20 15.60	5 5 5	0 0 0	430±10 430±10 430±10	2.50 3.00
PM 2000/EN 1522 PM 2000/EN 1522	PM6	7.62 x 39 mm AK-47 (M43) 5.56 x 45 mm SS109 (M855) 7.62 x 51 mm Nato Ball	8.00 4.00 9.55	10 10 10	0 0 0	720±10 950±10 830±10	4.25 6.50
PM 2000/EN 1522 Stanag 4569	PM7 Level 1	7.62 x 51 mm P80 Nato AP 7.62 x 51 mm Nato Ball 5.56 x 45 mm SS109 (M855) 5.56 x 45 mm M 193	9.45 9.55 4.00 3.56	10 30 30 30	0 0 0	820±10 833±20 900±20 937±20	14.20 9.20
Stanag 4569 Stanag 4569	Level 2 Level 3	7.62 x 39 mm AK-47 API BZ 7.62 x 51 mm AP (WC) 7.62 x 54R mm B32 API	7.77 8.40 10.30	30 30 30	0 0 0	695±20 930±20 945±20	12.20 25.10