Manganese Steel Plates
Manganese Steel Plates, Manganese Steel Plates Suppliers, Hadfield Manganese Plate Manufacturer, High Manganese Steel Plate Exporter in India.
ASTM A128 Gr B2 Plates, Hadfield Manganese Steel Plates Suppliers, Steel Plates, High Manganese Steel Plate Manufacturer.
We are one of the leading Manufacturers, Supplier and Exporters of wide range of Manganese Steel Plates. These are manufactured and designed using optimum quality raw material based on advanced machines technology. The Standard of this plates 12-14 % Manganese includes CREUSABRO, 12-14% Manganese Steel, head field manganese plate, manganese steel, ® M / X120 Mn12 / 12-14% Manganese.
These Manganese steel grades are widely demanded in various industries. Owing to its maximum wear resistant life, these plates are widely used in conveyor parts, grizzly bar, truck bed bodies and more.
Available range : Hadfield Manganese Plate & High Manganese Steel Plate
Features : Highly ductile, Non-magnetic properties, High tensile strength, Great welding ability and High abrasion resistance
Hadfield Manganese Plates
We have been able to hold a commendable market presence both in the international and domestic, by offering an unmatched array of Hadfield High Manganese Plates. These plates are used for making earth moving crusher jaw, grizzly, screen, stone chutes, chain guide and shredder plates. These hardened steel plates enhances almost five times the hardness of mild steel and almost three times the hardness of annealed stainless steel.
Technical Specifications :
| Hardness | Tensile | Yield | Will Work Hardened to | Elongation |
| 250BHN | 132,000 PSI | 90,000 PSI | 500BHN | 12% |
Application :
Quarries and constructions
Mines
Iron industry and foundry
Concrete and brick works
Scraps
Automotive industries
Standards :
| DIN | W1.3401 | EURONORM | 1.3401 � X120Mn13 |
| ASTM | A128 Gr B2 | AFNOR | X120Mn13 |
Chemical Analysis Typical values (% weight) :
| C | P | Mn | Mn | Si |
| 1.13 | ≤ 0.20 | 13 | 0.003 | 0.40 |
Mechanical Properties :
| Hardness HB | Yield Strength MPa | UTS MPa | El% | KCV 20�C (68�F) - J | |
| Typical Values | 220 | 380(55 KSI) | 940(136 KSI) | 40 | ≥ 112 J(≥ 83 ft.lbs) |
| Guaranteed Values | 180/245 | 350(51 KSI) | 800(116 KSI) | 30 | 64 J(47 ft.lbs) |
| after water quenching 980�C (1800�F) | |||||
Physical Properties :
| Density * | Expansion Coeff. 0-600�C | Specific Heat | Electrical * Resistivity | Thermal * Conductivity | Magnetic * Permeability | |
|---|---|---|---|---|---|---|
| Metric US | 7.88 | 10 -6�C1 21.5 10 -60�F-1 19.9 |
J/Metric Kg. �C 502 BTU/lb�F .12 |
�O.m 75 �O.m 75 |
W/m. �C 13 BTU/hr.ft�F 7.3 |
�1.002 |
High Manganese Steel Plate
We have been able to offer an extensive range of High Manganese Steel Plate. High Manganese Steel Plate is a non-magnetic and work hardening type of steel which thrives on severe wear conditions. The best thing about this kind of plate is that, the more impact and hammering it receives, the harder its surface becomes. These superior make 12-14 % Manganese is developed in line with the latest trends and norms set by the industry.
Composition :
| Manganese | Carbon |
| 132,000 PSI | 250BHN |
Application :
The High Manganese Steel Plate is used in
Wearing plates
Stone or iron chutes
Industrial track work
Anti drill plates such as security doors, shot blasting equipment and tumbling machines